CACAT LAS
|
|
SPATTERS , SURFACE POROSITY , PIN HOLE , SURFACE CRACKS , SURFACE COLD LAP , SURFACE CONCAVITY , SURFACE UNDERCUT , SURFACE UNDERFILL , EXCESSIVE REINFORCE MENT , WIDE BEAD , S TOP START , HIGH LOW |
|
|
|
ROOT POROSITY , ROOT CONCAVITY , ROOT CRACKS , BLOW HOLE , INCOMPLETE PENE-TRATION , EXCESSIVE PENETRATION , EX- CESS WIRE , ROOT UND ERCUT , ROOT UN- DERFILL . |
|
SLAG INCLUSION , SLAG LINES , INTERNAL POROSITY , WORM HOLES , INTERNALL COLD LAP , INCOMPLETE FUSION , INTERNAL CRACK , HOLLOW BEAD , ALIGNED POROSITY , HEAVY METAL INCLUSION , |
|
CACAT LAS
1. CUKUP DICHIP ( PAHAT ) SAJA ATAU DIKIKIR KASAR. TIDAK BOLEH DIGERINDA KARENA AKAN MEMAKAN PERMUKAAN BASE METALNYA . |
|
1. BURUK RUPA 2. MENGAWALI KARAT PER MUKAAN. |
|
1. LINGKUNGAN YANG BASAH ATAU LEMBAB 2. ELEKTODA LEMBAB 3. ANGIN MERASUK KE KOLAM LAS 4. BUSUR TERLALU PAN JANG . |
|
KRITERIA PENOLAKAN : JIKA TIDAK DIBERSIHKAN DAPAT MENYEBABKAN PENOLAKAN ( KARENA PENYELESAIANNYA YANG DIBAWAH STANDARD ) . |
|
POROSITY ( GELEMBUNG GAS ) |
|
1. GERINDA ATAU GOUGING HINGGA CACAT HILANG , DAN LAS ULANG SESUAI WPS RE PAIR.
|
|
1. TAMPAK JELEK 2. MELEMAHKAN SAMBUNG AN. 3. MENGAWALI KARAT PER MUKAAN. |
|
1. LINGKUNGAN BASAH ATAU LEMBAB 2. ELEKTRODA LEMBAB 3. AMPER CAPPING TER LALU TINGGI 4. TIMBUL GAS SEWAK TU PENGELASAN 5. LAPISAN GALVANIZE BELUM DIGERINDA 6. UDARA MERASUK KE DALAM KOLAM LAS 7. KAMPUH KOTOR |
|
KRITERIA PENOLAKAN SESUAI API 1104 : 1. SECARA INDIVIDUAL MELEBIHI 1/8 “ ATAU 25 % TEBAL NOMINAL . 2. DISTRIBUSINYA MELEBIHI KETENTUAN API 1104 GAMBAR 15 DAN 16. 3. UNTUK POROSITY BERKELOMPOK ( CLUSTER ) BERDIAMETER MELEBIHI 1/2 “ , JUMLAH PANJANG CLUSTER DALAM 12 “ LAS MELEBIHI 1/2 “ .
|
|
5. ARUS CAPPING TER LALU TINGGI 6. SALAH JENIS ARUS 7. SALAH JENIS POLA RITAS. 8. LAPISAN GALVANIIZE BELUM DIGERINDA. |
|
SURFACE CONCAVITY
|
|
|  |
|
|  |
|
|
KRITERIA PENOLAKAN : CACAT INI JIKA TIDAK DIPERBAIKI AKAN MENYEBABKAN PENOLAKAN ( KARENA TERMASUK CACAT YANG BERBAHAYA ). |
|
|
|
|  |
|
|
KRITERIA PENOLAKAN : PENOLAKAN ATAU PENERIMAAN BERSYARAT TERGANTUNG HASIL UJI N.D.T. JIKA TERBUKTI SELURUH LAJUR DILAS DENGAN AMPER RENDAH , JALUR LAS DITOLAK , DAN SEBALIKNYA JIKA MEMENUHI SYARAT JALUR DITERIMA DENGAN SYARAT TONJOLAN DISTANDARDKAN. CATATAN : KETINGGIAN REINFORCEMENT LAS MAXIMUM LIHAT KETENTUAN PADA HIGH LOW ( ANSI B 31.3 ) . |
|
|
|
|
|
|
|  |
|
|  |
|
|
KRITERIA PENOLAKAN : 1. UNTUK YANG MENONJOL BERULANG DAPAT DITERIMA DENGAN SYARAT DIGERINDA HINGGA BENTUK STANDARD . 2 . UNTUK YANG KOSONG DAPAT DITERIMA ASAL DIPERBAIKI DENGAN MENGISI CAPPING HINGGA BENTUK JALUR LAS UNIFORM. JIKA HAL TERSEBUT DIATAS TIDAK DILAKSANAKAN , JALUR LAS DITOLAK . |
|
1. GERINDA COLD LAP SEHING GA LEBAR JALUR LAS WA JAR. 2. BAHAN INDUK ( BASE MA- RIAL HARUS DIGANTI BARU ( JIKA ADA ) , DISTEL DAN DILAS ULANG SESUAI WPS ASLI . SELURUH WELDING CREW DIREJECT DAN DIGANTI ( KA RENA TELAH MEMANIPULA SI MUTU SECARA KRIMINAL ( TIDAK BERTANGGUNG JA WAB ) . |
|
1. UNTUK WIDE BEAD YANG BUKAN MANI PULASI MUTU : a) SURFACE COLD LAP KANAN KIRI SISI LAS. 2. UNTUK WIDE BEAD HASIL MANIPULASI MUTU : a) FATAL, BAHAN DA SAR HARUS DIGAN TI. |
|
1. WIDE BEAD YANG BUKAN HA- SIL MANIPULASI MUTU : a) SUHU METAL RELATIF DI- NGIN b) AYUNAN TERLALU MELE BAR c) JURU LAS TIDAK QUALI FIED. 2. WIDE BEAD HASIL MANIPULA SI MUTU. a) GAP SANGAT LEBAR b) JURU LAS DIPAKSA UN TUK MENSIASATINYA . c) GAP DISUMPAL DENGAN BENDA ASING . |
|
BENDA ASING UNTUK MENYUMPAL GAP |
|
CELAH / GAP TERLALU LEBAR |
|
HIGH LOW ( TINGGI RENDAH ) |
|
|
|
|
KRITEROA PENOLAKAN : 1. KETENTUAN ANSI B31.3 : t ≤ ¼ “ max. 1.5 mm ( 1/16 “ ) UNTUK EXTERNAL t > ¼ ~ ≤ 13 mm ( ½ “ ) , max. 3 mm ( 1/8” ) t > 13 mm ( ½ “ ) ~ ≤ 25 mm ( 1” ) ,max 4 mm ( 5/32 “ ) t > 25 mm ( 1 “ ) , max 5 mm ( 3/16 “ ) UNTUK INTERNAL = 2 X EXTERNAL JIKA MELEBIHI KETENTUAN TERSEBUT DIATAS HARUS DISERONG , KALAU TIDAK DILAKSANAKAN , DITOLAK . 2. KETENTUAN API 1104 : 1). JIKA SALAH SATU SISI AKAR LAS TERBU KA > 2 INCI SECARA INDIVIDUAL. 2.) DALAM 12” PANJANG LAS > 3 “ |
|
|
|  |
|
|  |
|
|
|
|
|
|  |
|
|  |
|
|
KRITERIA PENOLAKAN : JIKA BERLEBIHAN DITOLAK DAN HARUS DIHILANGKAN ( DIPERBAIKI ) KRITERIA PENERIMAAN SESUAI ANSI B31.1 : UNTUK KATEGORI NORMAL DAN SEVERE CYCLIC CONDITION KETINGGIAN ROOT EXCESSIVE PENETRATION ADALAH SBB.: t ≤ ¼ “ max. 1.5 mm ( 1/16 “ ) t > ¼ ~ ≤ 13 mm ( ½ “ ) , max. 3 mm ( 1/8” ) t > 13 mm ( ½ “ ) ~ ≤ 25 mm ( 1” ) ,max 4 mm ( 5/32 “ ) t > 25 mm ( 1 “ ) , max 5 mm ( 3/16 “ ) UNTUK KATEGORI D FLUID SERVICE : MAX. 2 X LIMIT DIATAS
|
|
|
|
|  |
|
|
KRITERIA PENOLAKAN SESUAI API 1104 : JIKA JUMLAH PANJANG LEBIH DARI 2 “ DALAM 12” PANJANG LAS ATAU JUMLAH PANJANG LEBIH DARI ¼ PANJANG LAS SECARA KESELURUHAN , DITOLAK . KRITERIA PENERIMAAN SESUAI ANSI B31.3 : UNTUK KATEGORI NORMAL , SEVERE CYCLIC DAN KATEGORI D , LONGITUDINAL GOOVE TIDAK ADA UNDERCUT , UNTUK SAMBUNGAN BRANCH ≤ 1 mm ( 1/32 “ ) DAN ≤ ¼ TEBAL NOMINAL LAS ( T W ) |
|
|
|
|
|
|
|
|
|  |
|
|
|  |
|
|  |
|
|  |
|
|
|  |
|
|
|
KRITERIA PENOLAKAN SESUAI API 1104 : 1. SECARA INDIVIDUAL MELEBIHI 1/8 “ ATAU 25 % TEBAL NOMINAL . 2. DISTRIBUSINYA MELEBIHI KETENTUAN API 1104 GAMBAR 15 DAN 16. 3. UNTUK POROSITY BERKELOMPOK ( CLUSTER ) BERDIAMETER MELEBIHI 1/2 “ , JUMLAH PANJANG CLUSTER DALAM 12 “ LAS MELEBIHI 1/2 “ . A PENOLAKAN |
|
C. INTERNAL
KRITERIA PENOLAKAN SESUAI API 1104 : 1. SECARA INDIVIDUAL > 1/8” LEBAR , 2. JUMLAH PANJANG MELEBIHI 3 X TEBAL PELAT . 3. SLAG LINES YANG PARALEL DIHITUNG SECARA MASING MASING APABILA MEMPUNYAI LEBAR > 1/32 “. 4. JUMLAH PANJANG DALAM 12” LAS > ½” , 5. DIDALAM PANJANG LAS 12” TERDAPAT LEBIH DARI 4 BUAH SLAG YANG MEMILIKI LEBAR 1/8”/ , UNTUK PIPA KECIL ( DIA.< 2 3/8” , SECARA INDIVIDUAL MEMILIKI LEBAR > ½ TEBAL NOMINAL PIPA DAN JUMLAH PANJANG > 2 X TEBAL NOMINAL PIPA. KRITERIA PENERIMAAN SESUAI ANSI B31.3 : 1. PANJANG INDIVIDUAL ≤ 1/3 TEBAL NOMINAL LAS. 2. LEBAR INDIVIDUAL ≤ 2.5 mm ( 3/32” ) ATAU ≤ 1/3 TEBAL NOMINAL LAS. 3. JUMLAH PANJANG DALAM 12 X TEBAL NOMINAL LAS ≤ TEBAL NOMINAL LAS . |
|
GENERAL LARGE / BESAR MERATA |
|
GENERAL FINE / HALUS MERATA |
|
|
|
|  |
|
|
KRITERIA PENOLAKAN SESUAI API 1104 : 1) SECARA INDIVIDUAL MELEBIHI 1/8 “ ATAU 25% TEBAL NOMINAL PIPA . 2) DISTRIBUSINYA MELEBIHI KETENTUAN API 1104 GAMBAR 15 DAN 16. 3) CLUSTER POROSITY TERJADI PADA CAPPING DENGAN DIAMETER > ½ “. 2) MENGANDUNG GAS POCKET DIDALAMNYA YANG BERUKURAN > 1/8”. KRITERIA PENERIMAAN INDIKASI PADA RADIOGRAFI YANG DIBULATKAN SESUAI ASME VIII. : SECARA RINCI DAPAT DILIHAT PADA APPENDIX 4 , ASME VIII . |
|
|
|
|
|
|
|  |
|
|
|
KRITERIA PENOLAKAN : DIDALAM STANDARD ASME , API MAUPUN ANSI , TIDAK DISPECIFY , JADI DIDASARKAN ATAS GOOD ENGINEERING PRACTICE ATAU INSPECTOR ‘ S JUDGEMENT ( PENDAPAT PROFESIONAL INSPECTOR ) . |
|
|
|  |
KELEMAHAN RADIOGRAFI
Untuk jenis cacat laminar ( bentuk bidang ) , radiografi ( x atau )
dalam posisi posisi cacat tertentu sulit atau sama sekali tidak dapat mendeteksinya ( posisi datar
atau 0 º dan 180 º tidak ada imagi samasekali ,
posisi 55 º , 125 º 235 º dan 305 º menghasilkan imagi
minimum , sehingga cacat pada posisi ini kadang terde
teksi kadang tidak. Yang tampak hanya cacat pada posisi diatas 55 º hingga dibawah 125 º , dan diatas
235 º hingga dibawah 305 º . Cacat seperti internal cold
lap dan laminasi tidak tampak samasekali pada film x-ray , sedangkan cacat seperti incomplete fusion dan
under bead crack sulit dideteksi
Pende teksian cacat ini hanya
dapat dilaksanakan dengan
meng gunakan ultrasonic flaw
detector dengan angle probe seperti sketsa dibawah ini :